The surface treatments at baseline led to statistically similar fatigue failure loads (953N-1313N), except for GLZ (1313N), which was significantly higher than 7%Si (953 N). Meanwhile, Ctrl had 40% pre-test failures (debonding) after aging, and therefore the worst fatigue performance (notable decrease in fatigue results), while all the other groups presented superior and statistically similar fatigue behavior (973-1271N). In fact, when considering baseline Vs aging conditions, stable fatigue results could only be noted when using surf