The increase in charge carrier concentration translates into much higher electrical conductivities and moderately lower Seebeck coefficients. These properties translate into power factors up to 2.1 mW m-1 K-2 at ambient temperature, well above those of PbS and PbS + CuxS. Additionally, the presence of multiple phases in the final composite results in a notable decrease in the lattice thermal conductivity. Overall, the introduction of metallic copper in the initial blend results in a significant improvement of the thermoelectric performance